by Gail Overton, senior editor, Laser Focus World
December 7, 2011 - Researchers at the Samsung Advanced Institute of Technology (Yongin, South Korea) and Seoul National University (Seoul, Korea) have demonstrated the first LEDs to be fabricated on amorphous glass substrates.
Because gallium nitride (GaN)-based LEDs grown on crystalline sapphire wafers are expensive and not amenable to large-sized wafer arrays, GaN LEDs on silicon substrates (GaN-on-Si) are an improved alternative. However, GaN LEDs on amorphous glass substrates offer even lower manufacturing costs, easier scalability to large-sized LED arrays, and potential use as emissive devices due to the transparency of the glass substrate material.
The secret to controlled growth of the five-period indium GaN/GaN (InGaN/GaN) multiple quantum wells that comprise the emissive layer in the pyramidal-shaped LED array is a thin-film titanium pre-orienting layer that is similar to the GaN hexagonal crystal structure. Following the pre-orienting layer and the initial low-temperature GaN layer (LT-GaN) is a hole-patterned silicon dioxide (SiO2) layer that further defines the nucleation sites for the emissive-layer growth stages using a local heteroepitaxy process. After polymerization of the pyramidal structures and a final indium tin oxide (ITO) electrode layer, the pyramidal LED devices were found to emit illumination in the range from 448–478nm with an approximate luminance of 600 cd/m2.
The research was published online by Nature Photonics.
This article was originally published by Laser Focus World and was reprinted with permission.
Print
Email
Save